NIOBIUM TYPE 1 & 2, UNS R04300, UNS R04210
NIOB1 (TYPE 1 REACTOR GRADE UNALLOYED)
NIOB2 (TYPE 2 COMMERCIAL GRADE UNALLOYED)
Strip, Coil, Foil , Wire, ASTM B393Shenzhen Sunrise Metal Industry Co.,Ltd 深圳市东升稀有金属有限公司
0086-0755-27185042
http://www.sunriseta.com
sales@sunriseta.com
http://www.sunriseta.com
sales@sunriseta.com
skype :Li.mary9
QQ : 1957953030
wahtsapp :15919982500
Applications
Type 1:
Used in jewelry, super-abrasives, thin film deposition (glass), high-energy physics, springs and superconducting magnets for aerospace, consumer electronics, medical and superconducting applications.
Used in jewelry, super-abrasives, thin film deposition (glass), high-energy physics, springs and superconducting magnets for aerospace, consumer electronics, medical and superconducting applications.
Type 2:
Used in jewelry, super-abrasives, thin film deposition (glass), high-energy physics, springs and superconducting magnets for aerospace, consumer electronics, medical and superconducting applications.
Used in jewelry, super-abrasives, thin film deposition (glass), high-energy physics, springs and superconducting magnets for aerospace, consumer electronics, medical and superconducting applications.
Description
Niobium is a very soft refractory metal with an extremely high melting point and corrosive resistant properties. High thermal/electric conductivity, easily fabricated and bio-compatible.
Chemistry: Ingot
| Element | Type 1 Reactor Grade | Type 2 Commercial Grade |
|---|---|---|
| Niobium | Balance | Balance |
| Carbon | 0.01 | 0.01 |
| Nitrogen | 0.01 | 0.01 |
| Oxygen | 0.015 | 0.025 |
| Hydrogen | 0.0015 | 0.0015 |
| Zirconium | 0.02 | 0.02 |
| Tantalum | 0.1 | 0.3 |
| Iron | 0.005 | 0.005 |
| Silicon | 0.005 | 0.005 |
| Tungsten | 0.03 | 0.05 |
| Nickel | 0.005 | 0.005 |
| Molybdenum | 0.020 | 0.020 |
| Hafnium | 0.02 | 0.02 |
| Titanium | 0.02 | 0.02 |
| Below Elements When Specified: | ||
| Boron | 2ppm | --- |
| Aluminum | 0.002 | 0.005 |
| Beryllium | 0.005 | --- |
| Chromium | 0.002 | --- |
| Cobalt | 0.002 | --- |
Physical Properties
Density, 0.310 lbs/in³, 8.66 g/cm³
Mean Coefficient of Thermal Expansion, in/in/°F (mm/m/°C)
70- 212°F (20- 100°C): 4.05 x 10-6(7.3)
70- 212°F (20- 100°C): 4.05 x 10-6(7.3)
Thermal Conductivity: (W/m-°K): (21°C): 53.7
Modulus of Elasticity, ksi (MPa)
1.52 x 10³ (104.9 x 10³) in tension
1.52 x 10³ (104.9 x 10³) in tension
Melting Point: 4490°F (2477°C)
Forms
Coil – Strip, Foil, Ribbon
Wire – Profile, Round, Flat, Square
Wire – Profile, Round, Flat, Square
Mechanical Properties at Room Temperature
ANNEALED: Typical
Ultimate Tensile Strength: 18 KSI min (124 MPa min)
Yield Strength (0.2% offset): 10.5 KSI min (72 MPa min)
Elongation:
Gauges: less than 0.010 inches: 15% min
Gauges: 0.010 inches and greater: 20% min
Ultimate Tensile Strength: 18 KSI min (124 MPa min)
Yield Strength (0.2% offset): 10.5 KSI min (72 MPa min)
Elongation:
Gauges: less than 0.010 inches: 15% min
Gauges: 0.010 inches and greater: 20% min
Niobium Type 1 and type 2 can be cold rolled to various tempers. Contact Shenzhen Sunrise Metal Industry Co.,Ltd 深圳市东升稀有金属有限公司Technical Service for additional information
Additional Properties
Corrosion Resistance:
Refer to NACE (National Association of Corrosion Engineers) for recommendations.
Refer to NACE (National Association of Corrosion Engineers) for recommendations.
Finishes:
#1–Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required.
#2D–Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process.
#2B–Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D.
#BA-Bright annealed cold rolled and bright annealed
#CBA-Course bright annealed cold rolled matte finish and bright anneal
#2-Cold Rolled
#2BA–Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part.
Polished-Various grit finish for specific polish finished requirements
*Not all finishes are available in all alloys – Contact Shenzhen Sunrise Metal Industry Co.,Ltd 深圳市东升稀有金属有限公司Sales for more information
#1–Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required.
#2D–Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process.
#2B–Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D.
#BA-Bright annealed cold rolled and bright annealed
#CBA-Course bright annealed cold rolled matte finish and bright anneal
#2-Cold Rolled
#2BA–Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part.
Polished-Various grit finish for specific polish finished requirements
*Not all finishes are available in all alloys – Contact Shenzhen Sunrise Metal Industry Co.,Ltd 深圳市东升稀有金属有限公司Sales for more information
Wire Finishes
XC-Extra clean. Bright annealed or bright annealed and cold rolled
Grease-Shenzhen Sunrise Metal Industry Co.,Ltd 深圳市东升稀有金属有限公司 bright finish for decorative applications
Soap-Soap is not removed from tempered wire to act as a lubricant
*Contact Shenzhen Sunrise Metal Industry Co.,Ltd 深圳市东升稀有金属有限公司Wire for custom wire finishes
Grease-Shenzhen Sunrise Metal Industry Co.,Ltd 深圳市东升稀有金属有限公司 bright finish for decorative applications
Soap-Soap is not removed from tempered wire to act as a lubricant
*Contact Shenzhen Sunrise Metal Industry Co.,Ltd 深圳市东升稀有金属有限公司Wire for custom wire finishes
Heat Treatment
Niobium Type 1 or Type 2 are non hardenable by heat treatment. They can only be hardened by cold working
Niobium Type 1 or Type 2 are non hardenable by heat treatment. They can only be hardened by cold working
Welding
For best results refer to: SSINA’s “Welding of Stainless Steels and Other Joining Methods”Shenzhen Sunrise Metal Industry Co.,Ltd 深圳市东升稀有金属有限公司
For best results refer to: SSINA’s “Welding of Stainless Steels and Other Joining Methods”Shenzhen Sunrise Metal Industry Co.,Ltd 深圳市东升稀有金属有限公司
0086-0755-27185042
http://www.sunriseta.com
sales@sunriseta.com
http://www.sunriseta.com
sales@sunriseta.com
skype :Li.mary9
QQ : 1957953030
wahtsapp :15919982500
没有评论:
发表评论